Biological Characteristics of Decellularized Bovine Jugular Vein Valved Conduit Treated with Dyemediated Photo Oxidation

Abstract: Objective To evaluate the biological characteristics of decellularized bovine jugular vein valved conduit treated with dyemediated photo oxidation. Methods From July 2009 to July 2010, this study was carried out in Xijing Hospital affiliated to the Fourth Military Medical University. Forty bovine jugular vein valved conduits were obtained from Qinchuan scalpers aged between 2 to 6 years with the weight ranged from 200 to 400 kg. Then, the 40 conduits were divided into four groups by random digital table with 10 in each group. The conduits were treated with glutaraldehyde in the glutaraldehyde group (GA group), were decellularized in the decellularized group (DC group), were decellularized and treated with dyemediated photo oxidation in the decellularized and dyemediated photo oxidation treated group (DP group) , and were not dealt with in the control group (CO group). Thickness, appearance, histology, water content, shrinkage temperature, breaking strength, and soluble protein level of the conduit wall and valve were detected and compared among the four groups. Results Thickness and water content of the conduit wall and valve in the DP group were similar to those in the CO group (Pgt;0.05), while thickness of both wall and valve in the DP group was less than those in the GA group (wall: 0.8±0.1 mm vs. 1.1±0.1 mm; valve: 02±0.1 mm vs. 0.3±0.1 mm, Plt;0.05), and water content of the conduit wall and valve in the DP group was more than those in the GA group (wall: 86.1%±2.2% vs. 70.4%±2.8%; valve: 87.1%±2.5% vs. 72.1%±3.1%, Plt;0.05). The breaking strength and shrinkage temperature of the DP group were similar to those of the GA group (Pgt;0.05), while the shrinkage temperature (wall: 84.7±1.4 ℃ vs. 70.4±0.3 ℃; valve: 85.7±1.5 ℃ vs. 70.7±0.6 ℃, Plt;0.05) and the breaking strength (wall: 10.4±1.1 N vs. 6.8±1.0 N; valve: 8.0±0.9 N vs. 3.2±0.6 N, Plt;0.05) of the DP group were higher than those in the CO group. Conclusion Decellularized bovine jugular vein valved conduits treated with dyemediated photo oxidation have nice biological characteristics.Key words: Dyemediated photo oxidation; Decellularized; Bovine jugular vein valved conduit; Biological characteristics